Foundry Ceramic Sand, teknụzụ aha ya dị ka “Sintered Ceramic Sand for Foundry”, akpọkwa ya dị ka ceramsite, ceramcast, otu na cerabeads, ụfọdụ mba na-akpọ Golden Sand, bụ ezigbo artificial okirikiri ọka udi nke a na-mere si calcined bauxite. Isi ọdịnaya ya bụ aluminum oxide na Silicon oxide. Aja ceramic, nwere ihe dị mma karịa nke ájá silica iji nweta arụmọrụ dị mma na ebe a na-emepụta ihe. Ọ nwere nnukwu refractoriness, obere mgbasawanye thermal, ezigbo ọnụọgụ angular, ọmarịcha mmiri na-efe efe, nnukwu iguzogide iyi, nchipịa na ujo thermal, ọnụ ọgụgụ dị elu.

Zitere anyị email

Nkọwa ngwaahịa

Mkpado ngwaahịa

Foundry Ceramic Sand, nke aha ya bụ "Sintered Ceramic Sand for Foundry", akpọkwara ya dị ka ceramsite, cerabeads, ceramcast, ụfọdụ mba a na-akpọkwa Golden Sand, bụ ezigbo ọka ọka okirikiri nke sitere na calcined bauxite. Isi ọdịnaya ya bụ aluminum oxide na Silicon oxide. Aja ceramic, nwere ihe dị mma karịa nke ájá silica iji nweta arụmọrụ dị mma na ebe a na-emepụta ihe. Ọ nwere nnukwu refractoriness, obere mgbasawanye thermal, ezigbo ọnụọgụ angular, ọmarịcha mmiri na-efe efe, nnukwu iguzogide iyi, nchipịa na ujo thermal, ọnụ ọgụgụ dị elu.

Ihe onwunwe seramiiki

Ihe mejupụtara kemịkalụ bụ isi	Al₂O₃≥53%, Fe₂O₃＜4%, TiO₂＜3%, SiO₂≤37%
Ụdị ọka	Spherical
Ọnụ ego angular	≤1.1
Akụkụ akụkụ	45μm-2000μm
Refractoriness	≥1800℃
Njupụta nnukwu	1.5-1.6 g/cm3
Mgbasa ọkụ (RT-1200℃)	4.5-6.5x10-6/k
Agba	Aja
PH	6.6-7.3
Ihe mejupụtara mineral	Dị nro + Corundum
Ọnụ ego acid	1 ml / 50g
LOI	0.1%

Uru

Kaist ceramic foundry sand is about half as light as zircon and chromite, is about third as light as fused ceramic sand. Compared to these natural sand and other foundry media (the material is able to turn out about twice the number of molds per unit weight). Kaist ceramic foundry sand can deliver mold and core packages with a range of benefits that include higher-strength sand casting packages, with high heat resistance, low thermal expansion, improved final part resolution and a smoother surface finish. It can also be handled very easily, saving labor and transfer power costs. However, the manufacturer recommends paying attention to the amount of binder addition.

Ngwa

Dị ka ihe na-anọpụ iche, KAIST seramiiki ájá na-adabara acid na alkali resins.

Enwere ike iji ya mee ihe n'ọtụtụ ebe maka igwe nkedo, ihe nkedo na igwe anaghị agba nchara, dị ka nkedo ụfụfụ furu efu, ájá mkpuchi, aja resin, igbe isi oyi, nkedo ziri ezi, na mbipụta 3D.

Golden-sand-for-sand-molding-castings-(6)

Ngwa

Golden-sand-for-sand-molding-castings-(3)

Mbukota na nnyefe

Golden-sand-for-sand-molding-castings-(4)

Mbukota na nnyefe

Akụkụ nke nkesa nha nha

Enwere ike ịhazi nkesa nha nha dị ka ihe ị chọrọ.

Ntupu		20	30	40	50	70	100	140	200	270	Pan	AFS
μm		850	600	425	300	212	150	106	75	53	Pan
Koodu	20/40	15-40	30-55	15-35	≤5							20±5
	30/50	≤1	25-35	35-50	15-25	≤10	≤1					30±5
	40/70		≤5	20-30	40-50	15-25	≤8	≤1				43±3
	70/40		≤5	15-25	40-50	20-30	≤10	≤2				46±3
	50/100			≤5	25-35	35-50	15-25	≤6	≤1			50±3
	100/50			≤5	15-25	35-50	25-35	≤10	≤1			55±3
	70/140				≤5	25-35	35-50	8-15	≤5	≤1		65±4
	140/70				≤5	15-35	35-50	20-25	≤8	≤2		70±5
	100/200					≤10	20-35	35-50	15-20	≤10	≤2	110±5