Ceramic foundry sand, technically named as “Sintered Ceramic Sand for Foundry”, some factories also named as ceramsite, cerabeads, ceramcast, is good artificial ball sand for foundries. Its main content is aluminum oxide and Silicon oxide. Ceramic foundry sand compare with Silica sand, it has high refractoriness, little thermal expansion, good angular coefficient, excellent flowability, high resistance to wear, crush and thermal shock, high reclamation rate, it could reduce the resin addition and coating amount, increasing your castings yield, more than ten times the number of reclamations. Compare with black ceramic sand, it has almost same properties except lower bulk density and higher more than 3 times reclamation. Sintered ceramic sand bulk density is 1.45-1.6 g/cm3, but black ceramic sand is 1.8-2.1 g/cm3.

Gửi email cho chúng tôi

Chi tiết sản phẩm

Thẻ sản phẩm

Thành phần hóa học chính	Al₂O₃≥53%, Fe₂O₃＜4%, TiO₂＜3%, SiO₂≤37%
Hình dạng hạt	hình cầu
Hệ số góc	≤1.1
Kích thước từng phần	45μm -2000μm
Tính khúc xạ	≥1800℃
Mật độ lớn	1,45-1,6 g/cm3
Giãn nở nhiệt（RT-1200oC）	4,5-6,5x10-6/k
Màu sắc	Cát
PH	6.6-7.3
Thành phần khoáng vật	Mềm + Corundum
Chi phí axit	＜1 ml/50g
LỢI	＜0,1%

Lợi thế

● Ceramic foundry sand offers longer work life and reduction of sand usage

● Ceramic foundry sand spherical shape compared with angular shaped grains allows for easier separation from cast parts and improved collapsibility resulting in lower scrap and casting efficiency

● Ceramic foundry sand offers lots of price savings compared with Zircon, Chromite, Black ceramic sand, Naigai cerabeads sand

● Safe to environment compared with Silica (silicosis) sand

● Lower thermal expansion and thermal conductivity. Casting dimensions are more accurate and lower conductivity provides better mold performance

● Cần ít nhựa hơn 30-50%

● Có thể sử dụng như một loại cát đơn

● Cung cấp trọng lượng riêng thực và diện tích bề mặt riêng thấp hơn

● Độ bền được cải thiện so với các loại cát đúc khác

Ứng dụng

As a neutral material, Ceramic foundry sand is both used to acid and alkali resins.

It can be widely used in all kinds of sand molding, such as resin-coated sand, self-setting resin sand, cold core box, green sand, precision casting, lost foam casting and 3D printing etc., excellent properties help you reduce more production cost.

ceramic foundry sand largest manufacture in China (2)

ceramic foundry sand largest manufacture in China (3)

ceramic foundry sand largest manufacture in China (6)

ceramic foundry sand largest manufacture in China (5)

Các bộ phận của phân bố kích thước hạt

Phân bố kích thước hạt có thể được tùy chỉnh theo yêu cầu của bạn.

Lưới thép		20	30	40	50	70	100	140	200	270	Chảo	AFS
μm		850	600	425	300	212	150	106	75	53	Chảo
Mã số	20/40	15-40	30-55	15-35	≤5							20±5
	30/50	≤1	25-35	35-50	15-25	≤10	≤1					30±5
	40/70		≤5	20-30	40-50	15-25	≤8	≤1				43±3
	70/40		≤5	15-25	40-50	20-30	≤10	≤2				46±3
	50/100			≤5	25-35	35-50	15-25	≤6	≤1			50±3
	100/50			≤5	15-25	35-50	25-35	≤10	≤1			55±3
	70/140				≤5	25-35	35-50	8-15	≤5	≤1		65±4
	140/70				≤5	15-35	35-50	20-25	≤8	≤2		70±5
	100/200					≤10	20-35	35-50	15-20	≤10	≤2	110±5