Ceramsite sand is an artificial spherical casting sand developed by SHXK, same with Japanese Cerabeads. It has high refractoriness (>1800°C), small angular coefficient (<1.1, approximately spherical), low acid consumption (neutral material), low binder content (at least 30% reduction in binder content), and particles high strength, non-breaking and other excellent characteristics, suitable for all types of sand foundry, especially for the coated sand. There are more successful application cases.
Polni keramični pesek se uporablja za izdelavo prevlečenega peska in se po predelavi večkrat ponovno uporabi, kar lahko učinkovito izboljša kakovost in proizvodno učinkovitost ulitkov, zmanjša stopnjo strganja ulitkov in proizvodne stroške podjetij, stroški dolgoročne uporabe pa so nižji od tega kremenčevega peska. Zato so v zadnjih letih skoraj vse velike tovarne premazanega peska uporabljale keramični pesek kot surovi pesek za proizvodnjo premazanega peska.
Prednost
● S smolo prevlečen keramični pesek s super visoko temperaturno odpornostjo, močno odpornostjo na intenzivnost deformacije, nizko napihnjenost, nizko nastajanje plina, za izpolnjevanje posebnih zahtev strank.
● Dobra sposobnost polnjenja fluidnosti, kalup proti prijemanju, uporaben za postopek izdelave umetnega jedra.
● Izjemno visoka temperaturna odpornost bi se lahko izognila napakam pri litju, kot so pekoč občutek, površinska guba, žile, bleščanje in razpoke.
● Small than 100kg castings could be achieved without sand coating.
Deli porazdelitve velikosti delcev
Porazdelitev velikosti delcev je mogoče prilagoditi glede na vaše zahteve.
|
Mreža |
20 | 30 | 40 | 50 | 70 | 100 | 140 | 200 | 270 | Pan | AFS | |
|
μm |
850 | 600 | 425 | 300 | 212 | 150 | 106 | 75 | 53 | Pan | ||
| Koda | 40/70 | ≤5 | 20-30 | 40-50 | 15-25 | ≤8 | ≤1 | 43±3 | ||||
| 70/40 | ≤5 | 15-25 | 40-50 | 20-30 | ≤10 | ≤2 | 46±3 | |||||
| 50/100 | ≤5 | 25-35 | 35-50 | 15-25 | ≤6 | ≤1 | 50±3 | |||||
| 100/50 | ≤5 | 15-25 | 35-50 | 25-35 | ≤10 | ≤1 | 55±3 | |||||
| 70/140 | ≤5 | 25-35 | 35-50 | 8-15 | ≤5 | ≤1 | 65±4 | |||||
| 140/70 | ≤5 | 15-35 | 35-50 | 20-25 | ≤8 | ≤2 | 70±5 | |||||
| 100/200 | ≤10 | 20-35 | 35-50 | 15-20 | ≤10 | ≤2 | 110±5 | |||||
Aplikacija
Blok motorja, glava valja, batni obroček, oljna tesnila, talna vzmet.
Majhno in srednje veliko nerjavno jeklo, lupina jeklene litine, brez jedra.
Used in large turbine shell mold, 6-8 speed gearbox, main part of auto brake disc,.
Večcilindrični blok (prazno obrnjeno jedro), izpušna cev in bronhus.
Odmična gred, oljno tesnilo, ohišje posode.
Vse vrste visokih standardov, visokih zahtev, težkega postopka prevlečenih peščenih ulitkov.