Ceramsite sand is an artificial spherical casting sand developed by SHXK, same with Japanese Cerabeads. It has high refractoriness (>1800°C), small angular coefficient (<1.1, approximately spherical), low acid consumption (neutral material), low binder content (at least 30% reduction in binder content), and particles high strength, non-breaking and other excellent characteristics, suitable for all types of sand foundry, especially for the coated sand. There are more successful application cases.
Ir-ramel taċ-ċeramika sħiħ jintuża biex jagħmel ramel miksi, u jerġa 'jintuża ripetutament wara r-reklamazzjoni, li jista' jtejjeb b'mod effettiv il-kwalità u l-effiċjenza tal-produzzjoni tal-ikkastjar, inaqqas ir-rata tal-brix tal-ikkastjar u l-ispiża tal-produzzjoni tal-intrapriżi, l-ispiża tal-użu fit-tul hija inqas minn dik tar-ramel tas-silika. Għalhekk, f'dawn l-aħħar snin, kważi l-impjanti kollha tar-ramel miksi fuq skala kbira użaw ramel taċ-ċeramika bħala ramel mhux maħdum biex jipproduċu ramel miksi.
Vantaġġ
● ramel taċ-ċeramika miksi bir-reżina b'reżistenza għat-temperatura għolja super, reżistenza qawwija għall-intensità tad-deformazzjoni, inflazzjoni baxxa, evoluzzjoni baxxa tal-gass, biex tissodisfa r-rekwiżiti speċjali tal-klijenti.
● Kapaċità tajba ta 'mili ta' fluwidità, moffa li ma twaħħalx, applikabbli għall-proċess artifiċjali ta 'teħid tal-qalba.
● Ir-reżistenza għat-temperatura super għolja tista 'tevita difetti tal-ikkastjar bħal ħruq tar-ramel, tinja tal-wiċċ, vening, flash tal-ġonta u xquq.
● Small than 100kg castings could be achieved without sand coating.
Partijiet tad-Distribuzzjoni tad-daqs tal-Partiċelli
Id-distribuzzjoni tad-daqs tal-partiċelli tista 'tiġi personalizzata skont il-ħtieġa tiegħek.
|
Malja |
20 | 30 | 40 | 50 | 70 | 100 | 140 | 200 | 270 | Pan | AFS | |
|
μm |
850 | 600 | 425 | 300 | 212 | 150 | 106 | 75 | 53 | Pan | ||
| kodiċi | 40/70 | ≤5 | 20-30 | 40-50 | 15-25 | ≤8 | ≤1 | 43±3 | ||||
| 70/40 | ≤5 | 15-25 | 40-50 | 20-30 | ≤10 | ≤2 | 46±3 | |||||
| 50/100 | ≤5 | 25-35 | 35-50 | 15-25 | ≤6 | ≤1 | 50±3 | |||||
| 100/50 | ≤5 | 15-25 | 35-50 | 25-35 | ≤10 | ≤1 | 55±3 | |||||
| 70/140 | ≤5 | 25-35 | 35-50 | 8-15 | ≤5 | ≤1 | 65±4 | |||||
| 140/70 | ≤5 | 15-35 | 35-50 | 20-25 | ≤8 | ≤2 | 70±5 | |||||
| 100/200 | ≤10 | 20-35 | 35-50 | 15-20 | ≤10 | ≤2 | 110±5 | |||||
Applikazzjoni
Blokk taċ-ċilindru tal-magna, ras taċ-ċilindru, ċirku tal-pistun, siġill taż-żejt, rebbiegħa tal-art.
Azzar li ma jissaddadx ta 'daqs żgħir u medju, qoxra tal-ikkastjar tal-azzar, off-core.
Used in large turbine shell mold, 6-8 speed gearbox, main part of auto brake disc,.
Blokk multi-ċilindru (qalba tat-tip flip vojta), il-pajp tal-egżost u l-bronku.
Camshaft, siġill taż-żejt, qoxra tal-kantuniera tal-kontenitur.
Kull tip ta 'standard għoli, rekwiżit għoli, proċess diffiċli ta' kkastjar tar-ramel miksi.