Ceramsite sand is an artificial spherical casting sand developed by SHXK, same with Japanese Cerabeads. It has high refractoriness (>1800°C), small angular coefficient (<1.1, approximately spherical), low acid consumption (neutral material), low binder content (at least 30% reduction in binder content), and particles high strength, non-breaking and other excellent characteristics, suitable for all types of sand foundry, especially for the coated sand. There are more successful application cases.
Volle keramieksand word gebruik om bedekte sand te maak, en herhaaldelik na herwinning hergebruik, wat die kwaliteit en produksiedoeltreffendheid van gietstukke effektief kan verbeter, die gietstukskraaptempo en die produksiekoste van ondernemings kan verminder, die langtermyngebruikskoste is laer as dit van silikasand. Daarom het byna alle grootskaalse bedekte sandplante in onlangse jare keramieksand as rou sand gebruik om bedekte sand te produseer.
Voordeel
● Hars bedekte keramiek sand met super hoë temperatuur weerstand, sterk weerstand teen vervorming intensiteit, lae inflasie, lae gas evolusie, om aan die spesiale vereistes van kliënte te voldoen.
● Goeie vloeibaarheidsvulvermoë, kleefvrye vorm, toepaslik vir die kunsmatige kernmaakproses.
● Superhoë temperatuurweerstand kan voorkom teen gietdefekte soos sandbrand, oppervlakvou, aar, gewrigflits en krake.
● Small than 100kg castings could be achieved without sand coating.
Dele van Deeltjiegrootteverspreiding
Die deeltjiegrootteverspreiding kan volgens u vereiste aangepas word.
|
Maas |
20 | 30 | 40 | 50 | 70 | 100 | 140 | 200 | 270 | Pan | AFS | |
|
μm |
850 | 600 | 425 | 300 | 212 | 150 | 106 | 75 | 53 | Pan | ||
| kode | 40/70 | ≤5 | 20-30 | 40-50 | 15-25 | ≤8 | ≤1 | 43±3 | ||||
| 70/40 | ≤5 | 15-25 | 40-50 | 20-30 | ≤10 | ≤2 | 46±3 | |||||
| 50/100 | ≤5 | 25-35 | 35-50 | 15-25 | ≤6 | ≤1 | 50±3 | |||||
| 100/50 | ≤5 | 15-25 | 35-50 | 25-35 | ≤10 | ≤1 | 55±3 | |||||
| 70/140 | ≤5 | 25-35 | 35-50 | 8-15 | ≤5 | ≤1 | 65±4 | |||||
| 140/70 | ≤5 | 15-35 | 35-50 | 20-25 | ≤8 | ≤2 | 70±5 | |||||
| 100/200 | ≤10 | 20-35 | 35-50 | 15-20 | ≤10 | ≤2 | 110±5 | |||||
Toepassing
Enjinsilinderblok, silinderkop, suierring, olieseël, vloerveer.
Klein en mediumgrootte vlekvrye staal, staalgietdop, buite-kern.
Used in large turbine shell mold, 6-8 speed gearbox, main part of auto brake disc,.
Muti-silinder blok (leë flip tipe kern), die uitlaatpyp en bronchus.
Nokas, olie seël, houer hoek dop.
Alle soorte hoë standaard, hoë vereiste, moeilike proses van bedekte sandgietwerk.